Stainless Steel Electrode

  • Product Details
  • Make an Inquiry

STAINLESS STEEL ELECTRODE

NAME

STANDARD

DIAMETER

(MM)

CHEMICAL COMPOSITION OF WELD METAL (%)

MECHANICAL PROPERTIES OF WLED METAL

CHARACTERISTICS AND APPLICATION

SH-A002

AWS E308L-16

BS 19.9.LAR

DIN E19 9LR23

GB E308L-16

JIS D308L-16

2.0

2.5

3.2

4.0

5.0

C ≤0.04

Mn 0.5-2.5

Si ≤0.90

Cr 18.0-21.0

Ni 9.0-11.0

S ≤0.030

P ≤0.040

TENSILE STRENGTH

≥ 520MPa

ELONGATION

≥35%

A LIME-TITANIA COATING AC/DC ELECTRODE FOR WELDING EXTRA LOW CARBON STAINLESS STEEL OR STRUCTUAL STEEL SUBJECTED TO WORKING TEMPERATURES BELOW

300°C AND CORROSION.

 

 

SH-A022

AWS E316L-16

BS 19.12.3.LAR

DIN E1912 3LR23

GB E316L-16

JIS D316L-16

2.0

2.5

3.2

4.0

5.0

C ≤0.04

Mn 0.5-2.5

Si ≤0.90

Cr 17.0-20.0

Ni 11.0-14.0

Mo 2.0-2.5

TENSILE STRENGTH

≥490MPa

ELONGATION

≥ 30%

A LIME-TITANIA COATING AC/DC ELECTRODE WITH AN EXTRA LOW CARBON CONTENT IN WELD METAL. IT IS INTENDED FOR WELDING Cr STAINLESS STEEL.

 

 

SH-A102

AWS E308-16

BS 19.9.AR

DIN E19 9R23

GB E308-16

JIS D308-16

2.0

2.5

3.2

4.0

5.0

C ≤0.08

Mn 0.5-2.5

Si ≤0.90

Cr 18.0-21.0

Ni 9.0-11.0

S ≤0.030

P ≤0.040

TENSILE STRENGTH

≥550MPa

ELONGATION

≥ 35%

ASTAINLESS ELECTRODE WITH LIMETITANIA COATING. SUITABLE FOR WELDING 0Cr19Ni9 OR 0Cr18Ni11Ti STAINLESS STEEL SUBJECTED TO WORKING TEMPERATURES BELOW 300°C AND CORROSION.

SH-A132

AWS E347-16

BS 19.9.Nb AR

DIN E19 9 Nb R23

GB E347-16

JIS D347-16

2.0

2.5

3.2

4.0

5.0

C ≤0.08

Mn 0.5-2.5

Si ≤0.90

Cr 18.0-21.0

Ni 9.0-11.0

Nb 8 x C-1.00

TENSILE STRENGTH

≥520MPa

ELONGATION

≥ 25%

A LIME-TITANIA COATING AC/DC ELECTRODE WITH NIOBIUM AS STABILIZING AGENT. IT IS SUITABLE FOR WELDING TITANIUM STABILIZED 0Cr18Ni 11 Ti STAINLESS STEEL SUBJECTED TO CORROSION.

SH-A202

AWS E316-16

BS 19.12.3.AR

DIN E19 12 3R23

GB E316-16

JIS D316-16

2.0

2.5

3.2

4.0

5.0

C ≤0.08

Mn 0.5-2.5

Si ≤0.90

Cr 17.0-20.0

Ni 11.0-14.0

Mo 2.0-3.0

TENSILE STRENGTH

≥520MPa

ELONGATION

≥ 30%

A LIME-TITANIA COATING AC/DC CURRENT. SUITABLE FOR WELDING 0Cr18Ni12Mo2 STAINLESS STEEL OR STRUCTURES SUBJECTED TO ACID. ALSO SUITABLE FOR WELDING THIN PLATES.

 

SHA102

AWS E309-16

BS 23.12.AR

DIN E23 12R23

GB E309-16 JIS D309-16

2.0

2.5

3.2

4.0

5.0

C ≤0.15

Mn 0.5-2.5

Si ≤0.90

Cr 22.0-25.0

Ni 12.0-14.0

TENSILE STRENGTH

≥550MPa

ELONGATION

≥ 25%

ALIME-TITANIA COATING ELECTRODE FOR WELDING STAINLESS STEEL, HIGH-Cr STEEL AND HIGH-Mn STEEL. SUITABLE FOR JOINING OF 308 STAINLESS STEEL TO MILD STEEL.